Fiberglass Direct roving refers to the glass fiber filament into a strand, not twisting directly on the bobbin.The last thread usually consists of 1,200 to 2,400 endless fibers.Glass roving is a kind of widely used glass fiber material.
Item | Unit | Data | Method |
Diameter | um | 13/12±1 | ISO 1888 |
Density | tex | 2400±5% | ISO 1889 |
Moisture | % | ≤0.1 | ISO 3344 |
IOI | % | 0.55±0.1 | ISO 1887 |
Stiffness | mm | 120±20 | ISO 3375 |
Item | Unit | Data | Method |
Diameter | um | 13/12±1 | ISO 1888 |
Density | tex | 2400±5% | ISO 1889 |
Moisture | % | ≤0.1 | ISO 3344 |
IOI | % | 0.5±0.15 | ISO 1887 |
Stiffness | mm | 110±20 | ISO 3375 |
Item | Unit | Data | Method |
Diameter | um | 13/12±1 | ISO 1888 |
Density | tex | 2400±5% | ISO 1889 |
Moisture | % | ≤0.1 | ISO 3344 |
IOI | % | 1.0±0.15 | ISO 1887 |
Stiffness | mm | 140±20 | ISO 3375 |
Item | Unit | Data | Method |
Diameter | um | 13/12±1 | ISO 1888 |
Density | tex | 2400±5% | ISO 1889 |
Moisture | % | ≤0.1 | ISO 3344 |
IOI | % | 0.55±0.1 | ISO 1887 |
Stiffness | mm | 130±20 | ISO 3375 |
Item | Unit | Data | Method |
Diameter | um | 12-14±1 | ISO 1888 |
Density | tex | 2400±5% | ISO 1889 |
Moisture | % | ≤0.1 | ISO 3344 |
IOI | % | 0.6±0.1 | ISO 1887 |
Stiffness | mm | 135±20 | ISO 3375 |
Fiberglass Direct roving refers to the glass fiber filament into a strand, not twisting directly on the bobbin.The last thread usually consists of 1,200 to 2,400 endless fibers.Glass roving is a kind of widely used glass fiber material.
Item | Unit | Data | Method |
Diameter | um | 13/12±1 | ISO 1888 |
Density | tex | 2400±5% | ISO 1889 |
Moisture | % | ≤0.1 | ISO 3344 |
IOI | % | 0.55±0.1 | ISO 1887 |
Stiffness | mm | 120±20 | ISO 3375 |
Item | Unit | Data | Method |
Diameter | um | 13/12±1 | ISO 1888 |
Density | tex | 2400±5% | ISO 1889 |
Moisture | % | ≤0.1 | ISO 3344 |
IOI | % | 0.5±0.15 | ISO 1887 |
Stiffness | mm | 110±20 | ISO 3375 |
Item | Unit | Data | Method |
Diameter | um | 13/12±1 | ISO 1888 |
Density | tex | 2400±5% | ISO 1889 |
Moisture | % | ≤0.1 | ISO 3344 |
IOI | % | 1.0±0.15 | ISO 1887 |
Stiffness | mm | 140±20 | ISO 3375 |
Item | Unit | Data | Method |
Diameter | um | 13/12±1 | ISO 1888 |
Density | tex | 2400±5% | ISO 1889 |
Moisture | % | ≤0.1 | ISO 3344 |
IOI | % | 0.55±0.1 | ISO 1887 |
Stiffness | mm | 130±20 | ISO 3375 |
Item | Unit | Data | Method |
Diameter | um | 12-14±1 | ISO 1888 |
Density | tex | 2400±5% | ISO 1889 |
Moisture | % | ≤0.1 | ISO 3344 |
IOI | % | 0.6±0.1 | ISO 1887 |
Stiffness | mm | 135±20 | ISO 3375 |